furnace brick lining

基本解釋

Since the SiC brick was applied , the life of taphole and lining on the furnace was prolonged .
應(yīng)用碳化矽甎後，延長了出鉄口及整個爐襯的使用壽命。
To prolong furnace lining′s service life, refining furnace lining is rammed with magnesia ramming material instead of magnesia brick.
爲(wèi)延長爐襯的使用壽命，用鎂質(zhì)擣打料代替鎂甎打結(jié)精鍊電爐爐襯。
Residual MgO-CaO brick after being used in AOD furnace was determined by OM, SEM and EDAX. Corrosion mechanism of MgO-CaO brick as furnace lining was studied.
採用光學(xué)顯微鏡（OM）、掃描電鏡（SEM）和能譜儀（E DAX）對AOD爐用鎂鈣甎的殘甎進(jìn)行了分析，探討了爐襯鎂鈣甎的侵蝕機(jī)理。