adhesion strength

基本解釋

The adhesion strength and stripping and splitting prevention measure were also discussed.
同時(shí)研究了涂料的粘附強(qiáng)度、防裂、防剝落等措施。
A(continuous) and compact electrode with the three-layer structure is formed at 950℃, and the adhesion strength of Ni electrodes is dependent on the middle layer.
燒結(jié)溫度是影響鎳電極致密化過(guò)程的重要因素，950℃時(shí)形成了連續(xù)、致密的三層結(jié)構(gòu)電極，中間層與鎳電極附著強(qiáng)度相關(guān)；
The results show that the interfacial adhesion strength increased noticeably for composites of active aramid fiber but the fracture energy of the interface decreased.
實(shí)驗(yàn)結(jié)果證明，芳綸表面改性顯著提高了其復(fù)合材料界面的粘結(jié)強(qiáng)度，相反卻降低了其界面斷裂能。

結(jié)合強(qiáng)度
Cross section micrographs and adhesion strength of the coatings were analyzed by TEM and scratch tester. The results show that:both the thickness of physical mixed interface layer and Cr bond layer was reduced significantly with the basic pressure decreased.
利用TEM、劃痕儀分析了不同真空度下鍍層微觀截面形貌與結(jié)合強(qiáng)度的變化。
粘接強(qiáng)度

結(jié)合強(qiáng)度
Interlayers and transition layers was introduced to improve the adhesion strength of the coatings.
通過(guò)引入中間過(guò)渡層的方法來(lái)提高涂層與基體的結(jié)合強(qiáng)度。
附著強(qiáng)度
Effects of the components and contents of binders on the thick film properties have been investigated. It was found that when the glass content was 10%, film adhesion strength achieve maximum (11.6MPa).
研究了玻璃粘結(jié)劑組成、含量對(duì)金屬化膜層性能的影響,實(shí)驗(yàn)發(fā)現(xiàn)當(dāng)玻璃含量為10%時(shí),Ag導(dǎo)體層與AlN基片之間附著強(qiáng)度最大(11.6MPa);在固含量不變的情況下,隨著玻璃含量的增加,方阻逐漸增大。
物理學(xué)
粘合強(qiáng)度
粘著強(qiáng)度
膠粘強(qiáng)度